Zhejiang Yuda Chemical Co.,Ltd.

Lithium silicate

• Category :

  Catalyst and Auxiliary

• Synonyms :

  Silicic acid, dilithium salt;Lithium silicate;silicic acid (h2sio3), dilithium salt;lithiumsilicate;Silicic acid,dilithium salt;LithiumMetasilicateAnhydrous; ;dilithium oxosilanediolate;

• CAS NO :

  10102-24-6

• EC NO :

  233-270-5

• Molecular Formula :

  Li₂O₃Si

• Molecular Weight :

  89.9657

• Main Specifications :

• InChI :

  InChI=1/2Li.O3Si/c;;1-4(2)3/q2*+1;-2

• Product description :

  special for water-based inorganic zinc-rich paint 1, overview The water-based inorganic zinc-rich paint is a new generation of environmentally friendly one, has the following characteristics which can be not reached by the organic epoxy zinc-rich paint: the good water-resisting property of the coating film, no smell, no pollution, not burning or explosion, simple construction, lower comprehensive cost and anti-corrosive lasting. It can be widely used in the production of water-based inorganic zinc-rich anti-corrosive coatings. 2, Product variety and parameters

  Designation	Standards
  	4.8?Lithium?silicate	6.5?Lithium?silicate	High-modulus potassium?silicate
  Molecular?formula	Li2O·mSiO2	Li2O·mSiO2	K2O·mSiO2
  Appearance	Transparent?liquid
  Modulus?M	4.8	6.5	5.5
  Density?(20°C,?g/cm3)	1.17-1.19	1.16-1.18	1.17-1.19
  Viscosity(20°C,?mPa?S)	﹤25	﹤25	﹤50
  PH?(20°C)	11-12	11.?-12	11.5-12..0
  Solid?content(wt,%)	22-23	22-23	25-28
  Particle?size?(nm)	8-15
  Stability	Six?months

  Designation	Standards
  	4.8?Lithium?silicate	6.5?Lithium?silicate	High-modulus potassium?silicate
  Molecular?formula	Li2O·mSiO2	Li2O·mSiO2	K2O·mSiO2
  Appearance	Transparent?liquid
  Modulus?M	4.8	6.5	5.5
  Density?(20°C,?g/cm3)	1.17-1.19	1.16-1.18	1.17-1.19
  Viscosity(20°C,?mPa?S)	﹤25	﹤25	﹤50
  PH?(20°C)	11-12	11.?-12	11.5-12..0
  Solid?content(wt,%)	22-23	22-23	25-28
  Particle?size?(nm)	8-15
  Stability	Six?months

  Designation	Standards
  	4.8?Lithium?silicate	6.5?Lithium?silicate	High-modulus potassium?silicate
  Molecular?formula	Li2O·mSiO2	Li2O·mSiO2	K2O·mSiO2
  Appearance	Transparent?liquid
  Modulus?M	4.8	6.5	5.5
  Density?(20°C,?g/cm3)	1.17-1.19	1.16-1.18	1.17-1.19
  Viscosity(20°C,?mPa?S)	﹤25	﹤25	﹤50
  PH?(20°C)	11-12	11.?-12	11.5-12..0
  Solid?content(wt,%)	22-23	22-23	25-28
  Particle?size?(nm)	8-15
  Stability	Six?months

  The modulus and the content for SiO2 can be adjusted according to custom requirements.

• Molecular Structure :